Newly Machined Alumina Ceramic Porous Tube
- yunxing
- china
- According to the quantity ordered
- 3000-5000/month(Looking for distributors)
Porous alumina ceramics have:
A. Excellent heat resistance, high hardness and excellent chemical stability.
B. Ideal catalyst carrier.
C. It uses catalytic combustion to convert organic waste gas into non-toxic carbon dioxide and water.
Newly Machined Alumina Ceramic PorousTube
My factory looking for distributors.
Porous alumina ceramics have excellent heat resistance, high hardness and excellent chemical stability. It is an ideal catalyst carrier. It uses catalytic combustion to convert organic waste gas into non-toxic carbon dioxide and water.
Porous alumina ceramics can be used as humidity sensors. Its working principle is that water in the air is adsorbed on the porous surface, causing changes in the conductance of the material. That is, the greater the air humidity, the thicker the water layer adsorbed by the porous alumina ceramics. , The greater the conductivity of the sensor, so the humidity of the surrounding environment can be inferred based on the conductivity of the material.
Composition table
| NAME | CONTENT(%) |
| Al2O3 | 99.3-99.5(99.7) |
| SiO2 | 0.3-0.5 |
| CaO+MgO | 0.2-0.3 |
| K2O+Na2O | 0.2-0.35 |
| Fe2O3 | <0.1 |
| OTHER | <0.05 |
Alumina ceramic performance index (Notice of Correct in Leakeage Rate）
NO. | Property | Unit | Alumina |
1 | Al2O3 | % | >99.3 |
2 | SiO2 | % | - |
3 | Density | g/cm3 | 3.88 |
4 | Water absorption | % | 0.01 |
5 | Cold compressive strength | MPa | 350 |
6 | 20ºC leakage rates | Torr・L/sec | >10-11=1.33322×10-12Pa・m3/sec |
7 | Twisting in high temperature | mm | 0.2 allowed in 1600ºC |
8 | Bonding in high temperature | not bonded in 1600ºC | |
9 | 20-1000ºC coefficient ofthermalexpansion | mm.10-6/ºC.m | 8.2 |
10 | Thermal conductivity | W/m.k | 25 |
11 | Electric insulation strength | KV/mm | 20 |
12 | 20ºCdirect current insulation resistance | Ohm/cm | 1014 |
13 | High-temperature insulation resistance | 1000ºC MΩ | ≥0.08 |
1300ºC MΩ | ≥0.02 | ||
14 | Thermal shock resistance | 4 times not cracked in 1550ºC | |
15 | Maximum working temperature | ºC | 180 |
Our factory
Jinzhou Yunxing Industrial Ceramics Co., Ltd. was established in 2000, mainly producing various types of tubular ceramic products and various industrial parts with alumina content above 99.3%. The factory covers an area of 4000 square meters.
The company currently has 3 1800 ° C high-temperature furnaces and 2 1400 ° C low-temperature kilns independently designed and manufactured. The molding process is mainly based on grouting molding, and has other molding process equipment such as extrusion and hot die casting.
The company has 105 employees, including one senior ceramic engineer, three engineers, six overseas sales staff, and four professional after-sales staff.