High Purity Alumina Ceramic Crucible , Multi Capacity Alumina Crucible Boat
- yunxing
- jinzhou
- It depends on the quantity of the order
- 3.000-6.000/month(Looking for distributors)
A. Small experimental kiln, experimental electric furnace adjustment formula and other purposes. Melting metals, precious metals, optical glass
B. It can be used in shuttle kilns and push-board kilns to burn color materials, colorants, frit, pigments, luminescent materials, etc.
C. Used for the analysis and firing of rare earth and other mineral raw materials, and the firing of high-temperature products such as ceramic powder.
High Purity Alumina Ceramic Crucible , Multi Capacity Alumina Crucible Boat
(1) Alumina Ceramic Crucible high melting point, corrosion resistance, melting point 2050℃, can Be better resistance to Be, Sr, Ni, Al, V, Ta, Mn, Fe, Co and other molten metal erosion.It also has high resistance to NaOH, glass and slag.It does not interact with Si, P, Sb, Bi in inert atmosphere.
Other dimensions, price reference table
| NUMBER | L*W*H*WT(MM) | SHAPE | PRICE($) |
| 1 | 30*20*15*δ2 | Rectangle | 0.87 |
| 2 | 45*13/11*9 | Boat shape with ears | 0.87 |
| 3 | 48*50/10 | Trapezoid | 5.8 |
| 4 | 50*10*10*δ2 | Rectangle | 0.87 |
| 5 | 80*50*7*δ1.5 | Rectangle | 1.74 |
| 6 | 80*55*15*δ2.5 | Rectangle | 2.18 |
| 7 | 84*13/11*8 | Boat shape with ears | 0.88 |
| 8 | 100*10*10*δ2 | Rectangle | 1.16 |
| 9 | 100*20*20*δ2 | Rectangle | 1.75 |
| 10 | 100*30*30*δ1.5 | Rectangle | 3.05 |
| 11 | 100*40*18*δ2 | Rectangle | 2.34 |
| 12 | 100*50*30*δ4 | Rectangle | 6.77 |
| 13 | 105*22*14*δ2 | Rectangle | 2.33 |
| 14 | 184*123*62*δ5 | Rectangle | 34.78 |
| 15 | 200*100*50*δ2 | Rectangle | 26.11 |
| 16 | 300*36*18*δ3 | Rectangle | 20 |
| 17 | 300*45/30*20*δ2 | Trapezoid | 11.75 |
Alumina ceramic performance index (Notice of Correct in Leakeage Rate）
NO. | Property | Unit | Alumina |
1 | Al2O3 | % | >99.3 |
2 | SiO2 | % | - |
3 | Density | g/cm3 | 3.88 |
4 | Water absorption | % | 0.01 |
5 | Cold compressive strength | MPa | 350 |
6 | 20ºC leakage rates | Torr・L/sec | >10-11=1.33322×10-12Pa・m3/sec |
7 | Twisting in high temperature | mm | 0.2 allowed in 1600ºC |
8 | Bonding in high temperature | not bonded in 1600ºC | |
9 | 20-1000ºC coefficient ofthermalexpansion | mm.10-6/ºC.m | 8.2 |
10 | Thermal conductivity | W/m.k | 25 |
11 | Electric insulation strength | KV/mm | 20 |
12 | 20ºCdirect current insulation resistance | Ohm/cm | 1014 |
13 | High-temperature insulation resistance | 1000ºC MΩ | ≥0.08 |
1300ºC MΩ | ≥0.02 | ||
14 | Thermal shock resistance | 4 times not cracked in 1550ºC | |
15 | Maximum working temperature | ºC | 1800 |
Our factory
Jinzhou Yunxing Industrial Ceramics Co., Ltd. was established in 2000, mainly producing various types of tubular ceramic products and various industrial parts with alumina content above 99.3%. The factory covers an area of 4000 square meters.
The company currently has 3 1800 ° C high-temperature furnaces and 2 1400 ° C low-temperature kilns independently designed and manufactured. The molding process is mainly based on grouting molding, and has other molding process equipment such as extrusion and hot die casting.
The company has 105 employees, including one senior ceramic engineer, three engineers, six overseas sales staff, and four professional after-sales staff.
Alumina purity test report
Our after-sale service