Extruded Alumina Ceramic Tube/Pipe
- yunxing
- china
- According to the quantity ordered
- 3000-6000/month(Looking for distributors)
A. Alumina combines low thermal expansion, excellent thermal conductivity and high compressive strength to make these furnace tubes resistant to thermal shock.
B. Alumina tube models have higher dielectric properties and provide higher vacuum or protective atmosphere at extreme temperatures.
Extruded Alumina Ceramic Tube/Pipe
My factory looking for distributors.
Minerals containing alumina make up nearly 15% of the earth’s crust making it practically inexhaustible and versatile. Alumina combines low thermal expansion, superior thermal conductivity, and high-compressive strength to make these furnace tubes thermal-shock resistant. alumina tube models come with elevated dielectric properties and offer a higher vacuum or protective atmosphere at an extreme temperature.
All products through the German DIN standards: DIN43724 / DIN43725 / DIN40680
Our alumina tubes offer:
--Extreme high temperature stability under reducing, inert, and high-vacuum condition under high temperature up to 1800°C.
--Extreme wear and abrasion resistance.
--Chemical corrosion resistance under high temperature.
--High dielectric properties.
--Protective atmospheres or high vacuum at high-temperature to eliminate contamination or impurity.
Composition table
| NAME | CONTENT(%) |
| Al2O3 | 99.3-99.5(99.7) |
| SiO2 | 0.3-0.5 |
| CaO+MgO | 0.2-0.3 |
| K2O+Na2O | 0.2-0.35 |
| Fe2O3 | <0.1 |
| OTHER | <0.05 |
Alumina ceramic performance index (Notice of Correct in Leakeage Rate）
NO. | Property | Unit | Alumina |
1 | Al2O3 | % | >99.3 |
2 | SiO2 | % | - |
3 | Density | g/cm3 | 3.88 |
4 | Water absorption | % | 0.01 |
5 | Cold compressive strength | MPa | 350 |
6 | 20ºC leakage rates | Torr・L/sec | >10-11=1.33322×10-12Pa・m3/sec |
7 | Twisting in high temperature | mm | 0.2 allowed in 1600ºC |
8 | Bonding in high temperature | not bonded in 1600ºC | |
9 | 20-1000ºC coefficient ofthermalexpansion | mm.10-6/ºC.m | 8.2 |
10 | Thermal conductivity | W/m.k | 25 |
11 | Electric insulation strength | KV/mm | 20 |
12 | 20ºCdirect current insulation resistance | Ohm/cm | 1014 |
13 | High-temperature insulation resistance | 1000ºC MΩ | ≥0.08 |
1300ºC MΩ | ≥0.02 | ||
14 | Thermal shock resistance | 4 times not cracked in 1550ºC | |
15 | Maximum working temperature | ºC | 1800 |
Our factory
Jinzhou Yunxing Industrial Ceramics Co., Ltd. was established in 2000, mainly producing various types of tubular ceramic products and various industrial parts with alumina content above 99.3%. The factory covers an area of 4000 square meters.
The company currently has 3 1800 ° C high-temperature furnaces and 2 1400 ° C low-temperature kilns independently designed and manufactured. The molding process is mainly based on grouting molding, and has other molding process equipment such as extrusion and hot die casting.
The company has 105 employees, including one senior ceramic engineer, three engineers, six overseas sales staff, and four professional after-sales staff.
Our services
Looking forward to your letter and visit.